More*Model No.: | WF994 |
---|---|
*Place Of Origin: | China |
*Material: | Clay |
*Size: | 60*240*11mm |
*Color: | Grey |
*Packaging Details: | Carton with Pallet |
*Payment Terms: | TT; L/C; PayPal; Western Union |
*Port: | Xiamen Port |
*Delivery Time: | in 35 days |
*Certification: | CE, ISO |
The advantages of cost effective abrasion resistant full body tiles are highest mechanical loads possible and chemical resistance.
ITEM NO. |
WF994 |
SURFACE |
PLAIN SURFACE |
WEIGHT |
19.5kg/CTN |
PACKAGE |
60PCS/CTN |
SAND SIZE |
SMALL |
WATER ABSORPTION RATE |
4.2% |
TILE QUANTITIES |
|
BRICKS PER m² BASED ON |
SQUARE METERS |
55 PCS |
18.144m² |
Testing Items |
National Standard |
|
Length and Width |
Difference of average size and working size of a single tile |
+/-1.5 |
Difference of average size and working size of ten tiles |
+/-1.5 mm |
|
Thickness |
Difference of average size and working size of a single tile |
+/-1.0 mm |
Appearance Quality |
The defects can't be seen in one meter |
|
Water Absorption (E,%) |
3.0<average E<=6.0 |
|
Breaking Modulus (R, Mpa) |
average value R>=13 |
|
Fracture Strength (S, N) |
S>=800 |
|
Thermal shock resistance |
After 10 times testing, No crackle or crack |
|
Frosting resistance |
After 100 times recycling test, No crack spalling |
Terrracotta tiles raw material is natural clay, feldspar, sand etc. After natural drying, the raw material is pulverized
into powder. The materials will be put into extrusion machine after adding an appropriate water. The wet tiles need to
put natural environment for drying about 3 days, then 1.5 days in drying kiln. And 1.5 days in firing kiln. After that, the
tiles will be delivered to split line, in there one tile will be split into two pieces. Final procedure is packing.
Clay brick tile was firstly produced in German which was made from certain percentage of many kinds of clay and a small
amount of mountain flour by pre-mixing, powering mixing, vacuum extrusion, drying and kiln firing. The color of tiles are
quite similar to natural mineral. That is why some foreigners named it Terracotta Tiles. In Taiwan China, local people
named it ejection brick according to the extrusion work. In China mainland, it was named clay split brick basic on the split
work after firing. Actually if from the point of material, it should be called clay tile (Japanese name)
From the original of clay tile we can know that this kind of tile is made from a certain percentage of different sintering
degree clay, different colors and a small amount of mountain flour. However, the material of the hot-selling glazed ceramic
tiles and full body ceramic tiles in the market is on conversely, using more mountain flour and less clay.